STAINLESS STEEL ASTM A312 TP 420 TUBES MANUFACTURER IN INDIA, SUPPLIER, 1.4021 420 STAINLESS STEEL ERW TUBES, EXPORTER OF 420 STAINLESS STEEL WELDED TUBE IN INDIA

Stainless Steel 420 Tube Specification

Item
Stainless Steel 420 Tube
Standard
GB, AISI, ASTM, ASME, EN, BS, DIN, JIS
Type
Seamless / ERW / Welded / Fabricated / CDW
Outer Diameter Size
SEAMLESS – 1/2″ NB TO 18″ NB
WELDED / ERW- 1″ NB TO 16″ NB
EFW – 8″ NB TO 110″ NB
Form
420 Round Tubing, 420 Square Tubes, 420 Rectangular Tube, “U” Shape 420 Tubing, 420 Hydraulic Tubes
Wall Thickness
Schedule 10 To Schedule 160 (3 mm to 100 mm Thickness)
Length
01 Meter to 12.5 Meters, Single Random Length, Double Random Length And Customize Size  End: Plain End, Beveled End, Treaded
Delivery Conditions
As Rolled, Formed, Stress Relieved, Annealed, Hardened, Tempered, Cold Draw
Coating
Electropolish, Mechanical Polish, Satin Finish, Passivated
Testing
Product Analysis, Transverse Tension Test, Flattening Test, Etching Test, Radiographic Examination, Stabilizing Heat Treatment, Intergranular Corrosion Test, Weld Decay Test, Magnetic Particle Detection, Grain Size Test, NACE 0175, Dual Grade, PWHT (POST WELD HEAT TREATMENT), Flare Test, Bend Test, Hardness Test, Tensile Test etc
Dimension
All Tubes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM and ASME
Value Added Services
Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment
Packaging
Loose / Bundle / Wooden Pallet / Wooden Box / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector
Material Test Certificate
Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC

SS 420 Tube Packing: We focus on every procedure to assure quality, the package we usually take Tube with environmental poly bags, and then in free fumigation wooden cases. Also can accept customized package such as OEM by negotiation.

Dinesh Tube India offers just about everything to meet your Tube pack requirements. Lot of emphasis is placed on the packing and packaging . The AISI 420 Tube are packed in wooden corrugated boxes foiled in plastic wraps and bubble wraps.

420 Stainless Steel Tube Marking: All Tube are marked with size and specification. Or as per customer’s requirement; So, besides the fact that we can arrange freight transportation for you, we can before that:

Specifically mark parts or packages: Provide for a special packing according to what is required by the shipping method or by you. We mark the Tube as needed with the most suitable marking technique.

When packaging and packing, our experienced warehouse staff systematically takes the greatest precautions for your Alloy 420 Tube to be optimally protected during transportation. We pack the Tube according to the appropriate method: strapped pallet, wooden crate, overseas packing.

Stainless Steel 420 Tube Useful Information

Stainless Steel 420 Tube Chemical Composition :

CMnSiPSCr
4200.15
max
1.00
max
1.00
max
0.04
max
0.03
max
min: 12.0
max: 14.0

Stainless Steel 420 Tube Mechanical Properties :

Tempering Temperature (°C)Tensile Strength (MPa)Yield Strength
0.2% Proof (MPa)
Elongation
(% in 50mm)
Hardness Brinell
(HB)
Annealed *65534525241 max
399°F (204°C)1600136012444
600°F (316°C)1580136514444
800°F (427°C)1620142010461
1000°F (538°C)1305109515375
1099°F (593°C)103581018302
1202°F (650°C)89568020262
* Annealed tensile properties are typical for Condition A of ASTM A276; annealed hardness is the specified maximum

Stainless Steel 420 Tube Physical Properties :

Density
kg/m3
Thermal Conductivity
W/mK
Electrical
Resistivity
(Microhm/cm)
Modulus of
Elasticity
Coefficient of
Thermal Expansion
µm/m/°C
Specific Heat
(J/kg.K)
775024.9 at 212°F550 (nΩ.m) at 68°F200 GPa10.3 at 32 – 212°F460 at 32°F to 212°F
– at 932 °F10.8 at 32 – 599°F
17.7 at 32-1000°F

Extensive Inventory of 420 Stainless Steel Tube for Sale in india at Best Price

 

Sr. No.Product DescriptionOutside Diamter, OD (in mm)Wall Thickness, WT (in mm)
1420 Stainless Steel Round Tube6mm – 630mm0.5mm-30mm
2420 Stainless Steel Square Tubing12.7mm* 12.7mm to 300mm* 300mm0.5mm-30mm
3420 Stainless Steel Rectangular Tube 10*20mm to 100*200mm0.5mm-30mm
4420 Stainless Steel Colour Coated Tubing6mm to 630mm0.5mm-30mm
5420 Stainless Steel Ornamental Tubes12.7mm to 76.2mm0.5mm-2.0mm
6420 Stainless Steel Electropolished Tubes12.7mm to 250mm0.5mm-30mm
7420 Stainless Steel Slot Round Tube12.7mm to 76.2mm0.5mm-2.0mm
8420 Stainless Steel Triangle Tubing16mm to 85mm0.5mm-3.0mm
9420 Stainless Steel Hexagonal Tube13mm to 85mm0.5mm-2.0mm
10420 Stainless Steel Handrail Tube0.5mm-2.0mm
11420 Stainless Steel U Shaped Tube20mm to 200mm0.5mm-2.0mm
12420 Thin-Wall Stainless Steel Tube 22mm*0.7mm to 108mm*2.0mm0.5mm-2.0mm
13420 Inner/Outside Polished Stainless Steel Tubing12.5mm to 203.2mm1.0mm – 5mm
14420 Stainless Steel Capillary Tube0.28mm to 10mm0.08mm – 1.2mm
15420 Stainless Steel Seamless Tube6mm to 430mm0.8mm – 30mm

 

Stainless Steel 420 Tube Material Specifications

ASTM A312 420: Seamless and straight-seam welded austenitic tube intended for high temperature and general corrosive service. Filler metal not permitted during welding.

ASTM A358 420: Electric fusion welded austenitic tube for corrosive and/or high temperature service. Typically only tube up to 8 inch is produced to this specification. Addition of filler metal is permitted during welding.

ASTM A790 420: Seamless and straight-seam welded ferritic/austenitic (duplex) tube intended for general corrosive service, with a particular emphasis on resistance to stress corrosion cracking.

ASTM A409 420: Straight-seam or spiral-seam electric fusion welded large diameter austenitic light-wall tube in sizes 14” to 30” with walls Sch5S and Sch 10S for corrosive and/or high

ASTM A376 420: Seamless austenitic tube for high temperature applications.

ASTM A813 420: Single-seam, single- or double- welded austenitic tube for high temperature and general corrosive applications.

ASTM A814 420: Cold-worked welded austenitic tube for high temperature and general corrosive service.